DC pulsed plasma magnetron sputtering of CdO/Cu/CdO multilayers thin films for self-cleaning and optoelectronic applications

Author name : ALZAHRAA ALY AHMED ABDELMOULA
Publication Date : 2023-03-13
Journal Name : J. Eur. Opt. Society-Rapid Publ.

Abstract

In this study, CdO/Cu/CdO multilayers thin films were organized on glass substrates with different Cu intermetallic layer thickness engaging DC plasma magnetron sputtering. The optoelectronic properties and structural characteristics of the multilayers at various Cu intermetallic layer thicknesses which were varied from 4 to 16 nm were explored. The calculated band gap was reduced from 2.66 eV to 2.48 eV as the Cu intermetallic layer thickness increased from 4 to 16 nm. The refractive index and coefficient of extinction of CdO/Cu/CdO multilayers increased with increasing the Cu intermetallic layer thickness. The resistivity is reduced from 1.8 × 10−2 Ω cm for CdO single layer to reach a value of 2.7 × 10−4 Ω cm for CdO/Cu (16 nm)/CdO multilayer. Further, the sheet resistance is decreased from 1000 to 13.8 Ω/sq. with the variation in Cu intermetallic layer thickness from 0 to 16 nm. CdO/Cu (4 nm)/CdO multilayer film recorded the best figure of merit (2.3 × 10−4 Ω−1). After sunlight illumination for the multilayers, the surface wettability was improved and the contact angle recorded lowest value of nearly 24° for CdO/Cu (8 nm)/CdO and CdO/Cu (12 nm)/CdO.

Keywords

Optical properties / CdO/Cu/CdO multilayers / Surface wettability

Publication Link

https://doi.org/10.1051/jeos/2023009

Block_researches_list_suggestions

Suggestions to read

HIDS-IoMT: A Deep Learning-Based Intelligent Intrusion Detection System for the Internet of Medical Things
Ahlem . Harchy Ep Berguiga
Generalized first approximation Matsumoto metric
AMR SOLIMAN MAHMOUD HASSAN
Structure–Performance Relationship of Novel Azo-Salicylaldehyde Disperse Dyes: Dyeing Optimization and Theoretical Insights
EBTSAM KHALEFAH H ALENEZY
“Synthesis and Characterization of SnO₂/α-Fe₂O₃, In₂O₃/α-Fe₂O₃, and ZnO/α-Fe₂O₃ Thin Films: Photocatalytic and Antibacterial Applications”
Asma Arfaoui
تواصل معنا