Electrical and optical properties of well-dispersed MWCNTs/PVA nanocomposites under different pH conditions

Series of polymer nanocomposites films consisting of pretreated multiwalled carbon
nanotubes (PT-MWCNTs) and poly (vinyl alcohol) (PVA) were prepared at room tem-
perature. The MWCNTs were initially pretreated with 1.0 M sulfuric acid (PT-MWCNTs)
and then allowed to disperse in aqueous solutions at different pH values (2–14). It was
found that the dispersion of the PT-MWCNTs is a pH dependent. The best PT-MWCNTs
dispersion was obtained at pH ¼ 10. Films of PT-MWCNTs/PVA, at this optimum pH-
value, were then prepared by casting technique at different PT-MWCNTs weight fractions.
The resulted PT-MWCNTs/PVA films were characterized through the direct visualization,
Fourier transform infrared, and morphology test. Besides, current–voltage and direct
current electrical conductivity for PT-MWCNTs/PVA nanocomposites at 60Cshowed
that the conductivity mechanism was ohmic and the percolation threshold was around 0.8
wt% PT-MWCNTs. Optical results showed that PT-MWCNTs are homogeneously dis-
tributed in the neat PVA and optical gap is significantly decreased from 4.40 to 2.96 eV.